Lupoy®
GP5206F
聚碳酸酯+丙烯腈丁二烯苯乙烯
玻璃纖維增強材料
產品說明:
LUPOY 5000 series is PC/ABS alloy that combine the superior impact
strength and the heat resistance of PC with the processibility and ductility of
ABS. LUPOY GP-5206F is glass fiber reinforced PC/ABS alloy which offers good
processibility and heat resistance. The grade fits the requirement of
Underwriters Laboratories for UL 94 V-0(1/16") flammability ratings. The
flammability and processibility of this grade makes it suitable for
electric/electronics applications.
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
填料/增強材料
|
|
|
特性
|
|
|
用途
|
|
|
UL文件號
|
|
|
多點數據
|
-
Isothermal Stress vs. Strain (ISO 11403-1)
-
Secant Modulus vs. Strain (ISO 11403-1)
|
-
Specific Heat vs. Temperature (ISO 11403-2)
-
Viscosity vs. Shear Rate (ISO 11403-2)
|
|
|
|
比重
|
|
|
|
|
--
|
1.35
|
g/cm?
|
ASTM
D792
|
|
--
|
1340
|
kg/m?
|
ISO
1183 3
|
|
熔體體積流動速率 (260°C/5.0
kg)
|
12.3
|
cm?/10min
|
ISO
1133 3
|
|
收縮率 - 流動 (3.18 mm)
|
1.0 到 3.0
|
%
|
ASTM
D955
|
|
吸水率 (飽和)
|
0.10
|
%
|
ISO
62 3
|
|
洛氏硬度 (R 級)
|
117
|
|
ASTM
D785
|
|
拉伸模量
|
6300
|
MPa
|
ISO
527-2 3
|
|
拉伸應力
|
|
|
|
|
斷裂
|
96.0
|
MPa
|
ISO
527-2 3
|
|
--
|
93.2
|
MPa
|
ASTM
D638
|
|
伸長率
|
|
|
|
|
斷裂
|
4.0
|
%
|
ASTM
D638
|
|
斷裂
|
1.8
|
%
|
ISO
527-2 3
|
|
彎曲模量 (3.18 mm)
|
5690
|
MPa
|
ASTM
D790
|
|
彎曲強度 (屈服, 3.18
mm)
|
137
|
MPa
|
ASTM
D790
|
|
簡支梁缺口沖擊強度
|
|
|
ISO
179/1eA 3
|
|
-30°C
|
7.50
|
kJ/m?
|
|
|
23°C
|
8.20
|
kJ/m?
|
|
|
簡支梁沖擊強度
|
|
|
ISO
179/1eU 3
|
|
-30°C
|
35.9
|
kJ/m?
|
|
|
23°C
|
38.3
|
kJ/m?
|
|
|
懸壁梁缺口沖擊強度 (23°C)
|
69
|
J/m
|
ASTM
D256
|
|
熱變形溫度
|
|
|
|
|
0.45
MPa
|
135
|
°C
|
ISO
75-2 3
|
|
1.8 MPa,
未退火, 3.18 mm
|
120
|
°C
|
ASTM
D648
|
|
1.8
MPa
|
125
|
°C
|
ISO
75-2 3
|
|
玻璃轉化溫度 4
|
140
|
°C
|
ISO
11357-2 3
|
|
維卡軟化溫度 (50°C/h, B
(50N))
|
127
|
°C
|
ISO
306 3
|
|
線形膨脹系數
|
|
|
ISO
11359-2 3
|
|
流動
|
2.9E-5
|
cm/cm/°C
|
|
|
橫向
|
6.2E-5
|
cm/cm/°C
|
|
|
RTI Elec (1.70 mm)
|
60.0
|
°C
|
UL
746
|
|
RTI Imp (1.70 mm)
|
60.0
|
°C
|
UL
746
|
|
RTI (1.70 mm)
|
60.0
|
°C
|
UL
746
|
|
表面電阻率
|
> 1.0E+15
|
ohm
|
IEC
60093 3
|
|
體積電阻率
|
> 1.0E+13
|
ohm·m
|
IEC
60093 3
|
|
耐電強度
|
28
|
kV/mm
|
IEC
60243-1 3
|
|
相對電容率 (1 MHz)
|
3.10
|
|
IEC
60250 3
|
|
耗散因數 (1 MHz)
|
0.010
|
|
IEC
60250 3
|
|
漏電起痕指數
|
200
|
|
IEC
60112 3
|
|
UL 阻燃等級 (1.70 mm)
|
V-0
|
|
UL
94
|
|
一定厚度與小時下的阻燃等級 (1.70 mm,
UL)
|
V-0
|
|
ISO
1210 3
|
|
干燥溫度
|
80.0 到 100
|
°C
|
|
|
干燥時間
|
3.0 到 4.0
|
hr
|
|
|
料筒后部溫度
|
235 到 245
|
°C
|
|
|
料筒中部溫度
|
245 到 255
|
°C
|
|
|
料筒前部溫度
|
245 到 255
|
°C
|
|
|
射嘴溫度
|
245 到 255
|
°C
|
|
|
模具溫度
|
50.0 到 70.0
|
°C
|
|
|
注塑壓力
|
58.8 到 118
|
MPa
|
|
|
背壓
|
0.981 到 3.92
|
MPa
|
|
|
螺桿轉速
|
40 到 80
|
rpm
|
|
|
Injection Pressure, secondary: 500 to
1000 kg/cm?
|
|