華東地區一級代理商沙比特塑料貿易（蘇州）有限公司 誠信經營 價格公道 質量保證 貨源充足 江浙滬現貨供應 SABIC Cycoloy C6800歡迎新老客戶前來咨詢與采購！
產品描述
CYCOLOY PC/ABS C6800物性表
非氯化、非溴化阻燃PC/ABS。
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL機械性能
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min / 抗拉強度,屈服,類型I,50 mm/min
|
62
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸長, 屈服, 類型I, 50 mm/min
|
5
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸長,斷裂,類型I, 50 mm/min
|
50
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min
|
2680
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 撓曲強度, 屈服, 1.3 mm/min, 50 mm 跨距
|
103
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span / 撓曲模量, 1.3 mm/min, 50 mm 跨距
|
2680
|
MPa
|
ASTM D 790
|
|
Hardness, Rockwell R / 硬度, 洛氏 R
|
120
|
–
|
ASTM D 785
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C / 懸臂梁缺口沖擊強度23°C
|
587
|
J/m
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C / 儀表控制抗沖擊總能量，23°C
|
67
|
J
|
ASTM D 3763
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed / 熱變形溫度,0.45 MPa, 3.2 mm,未退火
|
109
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 3.2mm, unannealed / 熱變形溫度,1.82 MPa, 3.2mm,未退火
|
98
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow / 線形膨脹系數,-40°C 到40°C,流動
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow / 線形膨脹系數,-40°C 到40°C,橫向
|
7.2E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity / 導熱系數
|
0.2
|
W/m-°C
|
ASTM C 177
|
|
Relative Temp Index, Elec / 相對熱指數， 電性能
|
90
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對熱指數，機械沖擊性能
|
85
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對熱指數，非機械沖擊性能
|
90
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity/比重
|
1.19
|
–
|
ASTM D 792
|
|
Specific Gravity/比重, color
|
1.18
|
–
|
ASTM D 792
|
|
Water Absorption, 24 hours / 吸水率， 24小時
|
0.1
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 23C / 吸水率，平衡，23C
|
0.4
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 3.2 mm / 模塑收縮量，流動，3.2 mm
|
0.4 – 0.6
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 3.2 mm / 模塑收縮量，橫向，3.2 mm
|
0.4 – 0.6
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率, 260°C/2.16 kgf
|
11
|
g/10 min
|
ASTM D 1238
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity/體積電阻率
|
1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Surface Resistivity
|
>1.E+14
|
Ohm
|
ASTM D 257
|
|
Dielectric Strength, in oil, 3.2 mm / 耐電強度，在油中，3.2mm
|
17.9
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 50/60 Hz / 相對介電常數，50/60 Hz
|
3
|
–
|
ASTM D 150
|
|
Relative Permittivity, 100 Hz
|
3
|
–
|
ASTM D 150
|
|
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz
|
0.0048
|
–
|
ASTM D 150
|
|
Hot Wire Ignition {PLC) / 熱絲引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC} / 高電流電弧引燃，表面{PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC} / 漏電起痕指數 (UL) {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS 火焰特性
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94V-1 Flame Class Rating (3) / UL認可,94V-1 阻燃等級(3)
|
1.47
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating (3) / UL認可,94V-0 阻燃等級(3)
|
2
|
mm
|
UL 94
|
|
UL Recognized, 94-5VB Rating (3) / UL認可,94-5VB 阻燃等級(3)
|
2.59
|
mm
|
UL 94
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature / 干燥溫度
|
75 – 80
|
°C
|
|
Drying Time / 干燥時間
|
2 – 4
|
hrs
|
|
Drying Time (Cumulative) / 干燥時間（累積的）
|
8
|
hrs
|
|
Maximum Moisture Content / 最大含濕量
|
0.04
|
%
|
|
Melt Temperature / 熔體溫度
|
230 – 265
|
°C
|
|
Nozzle Temperature / 注嘴溫度
|
230 – 265
|
°C
|
|
Front – Zone 3 Temperature / 前區3溫度
|
230 – 265
|
°C
|
|
Middle – Zone 2 Temperature / 中區2溫度
|
225 – 260
|
°C
|
|
Rear – Zone 1 Temperature / 后區1溫度
|
220 – 250
|
°C
|
|
Mold Temperature / 模具溫度
|
60 – 80
|
°C
|
|
Back Pressure / 背壓
|
0.3 – 0.7
|
MPa
|
|
Screw Speed / 螺桿速度
|
40 – 70
|
rpm
|
|
Shot to Cylinder Size / 每次注射量占料筒熔膠總量的百分比
|
30 – 80
|
%
|
|
Vent Depth / 排氣孔深度
|
0.038 – 0.076
|
mm
|
  
相關說明：正規的渠道進貨，可提供COA報告,MSDS,SGS環保報告,UL黃卡及物性加工參數，可開17%的增值稅發票，所售物資均為原廠原包，同時我們熱烈歡迎廣大客戶來公司進行監督考察。
相關承諾：我們希望能夠長期的與客戶合作，所以不謀取暴利，權衡利益，互利共贏！
訂購說明：貨物送達后，請時間檢查外包裝，如發現物流過程中出現大量包裝損壞及原料外漏的，請讓物流人員出具證明并保存，并在24小時內與我司相關人員取得聯系，我們會快速度解決問題。
|
在線咨詢 