TYPICAL PROPERTIES (1)
|
|
MECHANICAL機械性能
|
Value
|
Unit
|
Standard
|
|
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
|
17
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, break, 5 mm/min / 抗張程度,斷裂,5mm/min
|
90
|
MPa
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min / 拉伸伸長,斷裂,5mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
|
6000
|
MPa
|
ISO 527
|
|
Flexural Stress, break, 2 mm/min
|
120
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min / 彎曲模量,2 mm/min
|
5500
|
MPa
|
ISO 178
|
|
Hardness, H358/30 / 球壓硬度，H358/30
|
125
|
MPa
|
ISO 2039-1
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod IMPACT, unnotched 80*10*3 +23°C
|
35
|
kJ/m2
|
ISO 180/1U
|
|
Izod IMPACT, unnotched 80*10*3 -30°C
|
35
|
kJ/m2
|
ISO 180/1U
|
|
Izod IMPACT, notched 80*10*3 +23°C / 懸壁梁缺口沖擊強度, 80*10*3 +23°C
|
7
|
kJ/m2
|
ISO 180/1A
|
|
Izod IMPACT, notched 80*10*3 -30°C / 懸壁梁缺口沖擊強度, 80*10*3 -30°C
|
6
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 簡支梁缺口沖擊強度，23°C，C80*10*3 sp=62mm
|
6
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 簡支梁缺口沖擊強度，-30°C，C80*10*3 sp=62mm
|
5
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
40
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
40
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy IMPACT, notched, 23°C
|
9
|
kJ/m2
|
ISO 179/2C
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Thermal Conductivity / 導熱系數
|
0.22
|
W/m-°C
|
ISO 8302
|
|
CTE, 23°C to 80°C, flow
|
3.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
–
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50 / 維卡軟化溫度 A級/50
|
155
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50 / 維卡軟化溫度 B級/50
|
147
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120 / 維卡軟化溫度,B級/120
|
145
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 熱變形溫度，0.45 MPa, 未退火, 100 mm 跨距
|
144
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 熱變形溫度，1.8 MPa, 未退火, 100 mm 跨距
|
139
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Mold Shrinkage on Tensile Bar, flow (2) / 收縮率，流動
|
0.2 – 0.5
|
%
|
SABIC Method
|
|
Density/密度
|
1.35
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
|
0.29
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
|
0.12
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
4
|
cm3/10 min
|
ISO 1133
|
|
OPTICAL
|
Value
|
Unit
|
Standard
|
|
Haze/霧度
|
NA
|
%
|
ASTM D 1003
|
|
Refractive Index /折射指數
|
NA
|
–
|
ISO 489
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Volume Resistivity/體積電阻率
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity, ROA / 表面電阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, shorttime, 1.0mm
|
20
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 0.8 mm / 耐電強度，在油中，0.8mm
|
33
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 1.6 mm / 耐電強度，在油中，1.6mm
|
25
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 3.2 mm / 耐電強度，在油中，3.2mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 50/60 Hz / 相對介電常數，50/60 Hz
|
3
|
–
|
IEC 60250
|
|
Relative Permittivity, 1 MHz / 相對介電常數，1 MHz
|
2.9
|
–
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz
|
0.001
|
–
|
IEC 60250
|
|
Dissipation Factor, 1 MHz / 耗散因素，1 MHz
|
0.01
|
–
|
IEC 60250
|
|
Comparative Tracking Index / 漏電起痕指數
|
150
|
V
|
IEC 60112
|
|
FLAME CHARACTERISTICS 火焰特性
|
Value
|
Unit
|
Standard
|
|
UL Compliant, 94V-1 Flame Class Rating (3)(4)
|
1.6
|
mm
|
UL 94 by GE
|
|
Glow Wire Flammability Index / 灼熱絲易燃指數 850°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Flammability Index / 灼熱絲易燃指數 960°C, passes at
|
1.6
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI) / 極限氧指數
|
37
|
%
|
ISO 4589
|