| 比重 | 1.37 g/cc | 1.37 g/cc | |
| 吸水率 | 1.6 % | 1.6 % | |
| 線性成型收縮率,Flow | 0.0020 cm/cm | 0.0020 in/in | |
| 線性成型收縮率，橫向 | 0.0080 cm/cm | 0.0080 in/in | |
| 熔體流動速率 | 45 g/10 min @Load 2.16 kg, Temperature 320 °C | 45 g/10 min @Load 4.76 lb, Temperature 608 °F | ASTM D1238 |
| Spiral Flow | 5.30 cm @Load 750 kg, Temperature 320 °C | 2.09 in @Load 1650 lb, Temperature 608 °F | 0.5mm diameter |
| 抗張強度 | 45.0 MPa | 6530 psi | Weld; ASTM D638 |
| 160 MPa | 23200 psi | ASTM D638 | |
| 屈服伸長率 | 0.60 % | 0.60 % | Weld; ASTM D638 |
| 4.0 % | 4.0 % | ASTM D638 | |
| 彎曲強度 | 205 MPa | 29700 psi | ASTM D790 |
| 彎曲模量 | 8.50 GPa | 1230 ksi | ASTM D790 |
| 懸壁梁缺口沖擊強度 | 1.05 J/cm | 1.97 ft-lb/in | ASTM D256 |
| 體積電阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| 介電常數 | 3.3 @Frequency 1.00e+10 Hz | 3.3 @Frequency 1.00e+10 Hz | ASTM D150 |
| 介電強度 | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| 介電損耗指數 | 0.0090 @Frequency 1.00e+10 Hz | 0.0090 @Frequency 1.00e+10 Hz | ASTM D150 |
| 相比耐漏電起痕指數(CTI) | >= 600 V | >= 600 V | ASTM UL746A |
| 熔融溫度 | 306 °C | 583 °F | |
| 載荷下熱變形溫度(1.8 MPa) | 290 °C | 554 °F | ASTM D648 |
| 玻璃化轉變溫度，Tg | 125 °C | 257 °F | |
| 可燃性(UL94) | HB | HB |