20Cr4E冷鐓冷擠壓用鋼棒
|
|
|
|
|
|
|
|
|
中國ISC
|
A20204
|
|
|
|
|
|
|
|
|
對應標準
|
GB T 6478-2001
|
|
|
|
|
|
|
|
|
冷鐓和冷擠壓用鋼
|
|
|
|
|
|
|
|
|
Steels for cold heading and cold extruding
|
|
|
|
|
|
|
|
|
歸類
|
合金鋼
|
|
|
|
|
|
|
|
|
20Cr4E化學元素成分含量(%)
|
|
|
|
|
|
|
|
|
|
成分
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni *
|
Cu *
|
Al ?
|
最小值
|
0.17
|
-
|
0.6
|
-
|
-
|
0.9
|
-
|
-
|
0.02
|
最大值
|
0.23
|
0.3
|
0.9
|
0.035
|
0.035
|
1.2
|
0.2
|
0.2
|
-
|
①經供需雙方協議,可供應其他牌號的冷鐓鋼和冷擠壓用鋼
|
|
|
|
|
|
|
|
|
|
②鋼材的化學成分允許偏差應符合GB/T 222-1984的相關規定。
|
|
|
|
|
|
|
|
|
|
?為鋼中的全鋁量
|
|
|
|
|
|
|
|
|
|
*為鋼中的殘余元素含量
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
20Cr4E機械性能
|
|
|
|
|
|
|
|
|
|
條件
|
熱處理或狀態
|
抗拉強度
|
屈服點
|
斷后伸長率或延伸率
|
斷面收縮率
|
|
|
|
|
σb
|
σs
|
δ
|
ψ
|
|
|
|
|
Mpa
|
Mpa
|
%
|
%
|
|
|
|
|
鋼材
|
退火
|
≤560
|
|
|
≥60
|
|
|
|
|
試樣直徑d=25
|
熱處理
|
750~1100
|
≥490
|
≥9
|
|
|
|
|
|
*鋼材直徑不大于12mm時,斷面收縮率可降低2%
|
|
|
|
|
|
|
|
|
|
※熱處理制度:
|
|
|
|
|
|
|
|
|
|
滲碳溫度880~980°C,直徑淬火溫度820~860°C,雙重淬火溫度 心部淬硬860~900°C 表面淬硬780~820°C,回火溫度150~200°C
|
|
|
|
|
|
|
|
|
|
以上溫度只是推薦值,實際選擇的溫度應以使性能達到要求為準。
|
|
|
|
|
|
|
|
|
|
滲碳溫度取決于鋼的化學成分和滲碳介質。一般情況下,如鋼直接淬火,不要超過950°C。
|
|
|
|
|
|
|
|
|
|
淬火劑的種類取決于產品形狀、冷卻條件和爐子裝料的數量。
|
|
|
|
|
|
|
|
|
|
回火時間推薦最少1h。
|
|
|
|
|
|
|
|
|
|