TFA |
AWS A5.9 |
熔敷金屬化學成分 |
|||||||||||||||||
|
C |
Si |
Mn |
Cr |
Ni |
Mo |
Cu |
Co |
Al |
Ti |
Fe |
Nb + Ta |
P |
S |
Others |
|||||
|
625MIG/TIG |
ERNiCrMo-3 |
0.1 |
0.5 |
0.5 |
22 |
>=60 |
9 |
0.5 |
1 |
0.4 |
0.4 |
5 |
3.5 |
0.015 |
0.015 |
|
|||
|
82MIG/TIG |
ERNiCr-3 |
0.1 |
0.5 |
3 |
20 |
>=67 |
- |
0.5 |
1 |
- |
0.8 |
3 |
2.5 |
0.03 |
0.015 |
|
|||
|
60MIG |
ERNiCu-7 |
0.15 |
1.25 |
3.5 |
- |
65 |
- |
Bal |
1 |
1.25 |
2.7 |
2.5 |
- |
0.02 |
0.015 |
|
|||
|
61MIG |
ERNi-1 |
0.15 |
0.75 |
1 |
- |
>=93 |
- |
0.25 |
1<,, /TD>, |
1.5 |
3 |
1 |
- |
0.03 |
0.015 |
|
|||
|
C276MIG/TIG/SAW |
ERNiCrMo-4 |
0.02 |
0.08 |
1 |
16 |
余量 |
16 |
0.5 |
2.5 |
- |
- |
5.5 |
- |
0.04 |
0.03 |
W + V + |
|||
|
C22MIG/TIG |
ERNiCrMo-10 |
0.15 |
0.08 |
0.5 |
- |
余量 |
13.5 |
0.5 |
2.5 |
21 |
0.7 |
4 |
- |
0.02 |
0.01 |
W + |
|||
|
型號 |
C |
Si |
Mn |
Cr |
HRC |
特征和用途 |
|||||||||||||
|
OK83.27 |
E1-UM-350 |
0.15 |
＜0.7 |
0.7 |
3.2 |
35 |
堿性焊條，用于抗金屬間磨損，典型應用包括鋼軌、鑄鋼齒輪、軋機部件 |
||||||||||||
|
OK83.28 |
E1-UM-300 |
0.1 |
＜0.7 |
0.7 |
3.2 |
30 |
堿性焊條，用于堆焊鋼軌、軸、軋機部件等，也用于連接硬化鋼 |
||||||||||||
|
OK83.29 |
E1-UM-300 |
0.1 |
0.5 |
0.7 |
3.2 |
30 |
鋯堿性焊條，用途同OK83.28 |
||||||||||||
|
OK83.50 |
E6-UM-55 |
0.4 |
＜0.6 |
＜1.0 |
6.0Mo0.6 |
50-60 |
鈦酸性焊條，用于修復農機，載重機械等磨損部件，交流焊接時，空載電壓需大于45V |
||||||||||||
|
OK83.53 |
E6-UM-60 |
0.5 |
0.8 |
1.3Bn0.6 |
7.4Mo1.3 |
58 |
堿性焊條，用于磨料磨損和磨料磨損與沖擊磨損同時存在的場合。典型應用包括巖石破碎機和鉆機 |
||||||||||||
|
OK83.65 |
E2-UM-60 |
0.8 |
4.0 |
＜0.6 |
2.0 |
58-63 |
堿性焊條，熔敷金屬硬度高，耐磨性好，抗氧化溫度大約為875℃，適合堆焊承受石塊、，煤、沙、土壤磨損的機器部件，典型應用是挖掘機、螺旋送料裝置，破碎機和拖拉機部件 |
||||||||||||
|
OK84.42 |
E5-UM-645-R |
0.12 |
0.5 |
＜0.5 |
13.0 |
39-45 |
鈦堿性焊條，熔敷金屬為耐腐蝕的馬氏體-鐵素體不銹鋼，適合堆焊軸，輪式輸送機，鑄鋼閥門座等 |
||||||||||||
|
OK84.52 |
E6-UM-55-GR |
0.25 |
0.5 |
＜0.5 |
13.0 |
49-55 |
鈦堿性焊條，熔敷金屬為耐腐蝕的馬氏體鋼，適合堆焊軸，輪式輸送機、鑄鋼閥門座、混料機臂、送料齒輪、刀具等。預熱和層間溫度約200℃ |
||||||||||||
|
OK84.58 |
E6-UM-55G |
0.7 |
0.6 |
0.7 |
10.0 |
53-59 |
堿性焊條，熔敷金屬為耐腐蝕的馬氏體鋼，無論冷卻速度如何，層就可以到達硬度要求。適合堆焊承受磨料和沖擊磨損的部件如農業機械、載重機和混料機 |
||||||||||||