不銹鋼、鎳基合金焊材(Stainless
Steels and Nickel Alloys)
|
|
不銹鋼鎢極氬弧焊實心料絲(GTAW rods
for Stainless Steels)
|
產品牌號
Thermanit…
|
分類標準及標號
|
基本化學成份典型值(%)
|
熱處理
|
σ0.2
|
σb
|
δ5
|
AKW
|
|
AWS A5.9
|
EN17072
|
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
Nb
|
Fe
|
N
|
其它
|
MPa
≥
|
MPa
≥
|
%
≥
|
℃
|
J
≥
|
|
A Si
|
≈ER318Si
|
W 19 12 3 Nb Si
|
0.05
|
1.5
|
0.8
|
19.0
|
12.0
|
2.8
|
>12×C
|
|
|
|
AW
|
390
|
600
|
30
|
+20
|
70
|
|
ATS 4
|
ER19-10H
|
W 19 9 H
|
0.05
|
1.8
|
0.3
|
18.8
|
9.3
|
|
|
|
|
|
AW
|
320
|
500
|
35
|
+20
|
70
|
|
C Si
|
≈ER310
|
W 25 20 Mn
|
0.13
|
3.2
|
1.0
|
25.0
|
20.5
|
|
|
|
|
|
AW
|
350
|
550
|
25
|
+20
|
80
|
|
|
不銹鋼鎢極氬弧焊實心焊絲(GTAW rods
for Stainless Steels)
|
產品牌號
Thermanit…
|
分類標準及標號海焊焊材
|
基本化學成份典型值(%)
|
熱處理
|
σ0.2
|
σb
|
δ5
|
AKW
|
|
AWS A5.9
|
|
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
Nb
|
Cu
|
N
|
其它
|
MPa
≥
|
MPa
≥
|
%
≥
|
℃
|
J
≥
|
|
CR
|
≈ER310
|
W 25 20 H
|
0.45
|
1.5
|
1.0
|
26.0
|
21.8
|
-
|
|
|
|
|
AW
|
400
|
600
|
10
|
-
|
-
|
|
D
|
≈ER309
|
W 22 12 H
|
0.11
|
1.2
|
1.2
|
22.0
|
11.0
|
-
|
|
|
|
|
AW
|
350
|
550
|
30
|
+20
|
70
|
|
GE-316L
|
ER316L
|
W 19 12 3 L
|
0.02
|
1.7
|
0.8
|
18.8
|
12.5
|
2.8
|
|
|
|
|
AW
|
380
|
560
|
35
|
+20
|
70
|
|
H-347
|
ER347
|
W 19 9 Nb
|
0.06
|
1.5
|
0.8
|
19.5
|
9.5
|
-
|
>12×C
|
|
|
|
AW
|
400
|
570
|
30
|
+20
|
65
|
|
JE-308L
|
ER308L
|
W 19 9 L
|
0.02
|
1.7
|
0.9
|
20.0
|
10.0
|
-
|
|
|
|
|
AW
|
350
|
570
|
35
|
-196
|
35
|
|
X
|
≈ER307
|
W 18 8 Mn
|
0.08
|
7.0
|
0.8
|
19.0
|
9.0
|
-
|
|
|
|
|
AW
|
370
|
600
|
35
|
+20
|
100
|
|
13/04 Si
|
≈ER410NiMo
|
W 13 4
|
0.03
|
0.7
|
0.8
|
13.0
|
4.7
|
0.5
|
|
|
|
|
600/8h
|
680
|
800
|
15
|
+20
|
50
|
|
14 K
|
≈ER410
|
W 13
|
0 .06
|
0 .6
|
0 .3
|
12 .5
|
1 .3
|
-
|
|
|
|
|
680/8h
|
450
|
650
|
15
|
+20
|
50
|
|
14 K Si
|
≈ER410
|
W 13
|
0 .08
|
0 .65
|
0 .9
|
14 .0
|
0 .4
|
-
|
|
|
|
|
680/8h
|
450
|
650
|
15
|
-
|
-
|
|
17
|
≈ER430
|
W 17
|
0.07
|
0.7
|
0.8
|
17.5
|
-
|
-
|
|
|
|
|
800/1h
|
340
|
540
|
20
|
-
|
-
|
|
17/15 TT
|
-
|
WZ 17 15 Mn W
|
0.2
|
10.5
|
0.4
|
17.5
|
14.0
|
|
|
|
|
W:3.5
|
AW
|
430
|
600
|
30
|
-196
|
50
|
|
1720
|
-
|
WZ 17 Mo
|
0.20
|
0.40
|
0.60
|
17.0
|
0.40
|
1.10
|
|
|
|
|
760/2h
|
500
|
700
|
15
|
-
|
-
|
|
1740
|
-
|
WZ 17 MoH
|
0.40
|
<0.5
|
<0.5
|
16.5
|
0.5
|
1.0
|
|
|
|
|
760/2h
|
600
|
800
|
12
|
-
|
-
|
|
18/17 E
|
≈ER317L
|
W 18 1 6 5N L
|
0.03
|
3.4
|
0.3
|
18.5
|
17.5
|
4.5
|
|
|
|
|
AW
|
320
|
570
|
34
|
+20
|
65
|
|
19/15 H
|
≈ER316L
|
W 20 16 3 Mn NL
|
0.03
|
7.5
|
0.5
|
20.5
|
15.5
|
3.0
|
|
|
0.18
|
|
AW
|
430
|
650
|
30
|
+20
|
80
|
|
20/10
|
≈ER308Mo
|
W 20 10 3
|
0.05
|
1.3
|
0.5
|
20.5
|
10.5
|
3.3
|
|
|
|
|
AW
|
470
|
670
|
25
|
+20
|
50
|
|
20/16 SM
|
-
|
W 20 17 3 Mn N L
|
0.03
|
7.3
|
0.7
|
22.2
|
18.0
|
3.6
|
|
|
0.24
|
|
AW
|
430
|
640
|
30
|
+20
|
70
|
|
20/25 Cu
|
ER385
|
W 20 25 5 Cu L
|
≤0.025
|
2.5
|
0.2
|
20.2
|
25.0
|
4.8
|
|
1.5
|
|
|
AW
|
350
|
550
|
35
|
+20
|
55
|
|
21/33
|
-
|
WZ 21 32 Nb
|
0.20
|
2.3
|
0.2
|
22.0
|
33.0
|
-
|
1.7
|
|
|
|
AW
|
380
|
600
|
25
|
+20
|
50
|
|
21/33 So
|
-
|
WZ 21 32 Nb Mn
|
0.12
|
4.8
|
0.2
|
22.0
|
33.0
|
-
|
1.2
|
|
|
|
AW
|
380
|
600
|
25
|
+20
|
50
|
|
22/09
|
ER2209
|
W 22 9 3 L N
|
0.025
|
1.6
|
0.5
|
23.0
|
9.0
|
3.0
|
|
|
0.14
|
|
AW
|
510
|
680
|
20
|
+20
|
50
|
|
25/07 CuT
|
≈ER2553
|
W 25 7 4 L
|
0.02
|
0.8
|
0.5
|
25.5
|
7.0
|
3.7
|
|
0.6
|
0.2
|
W:0.6
|
AW
|
600
|
750
|
25
|
-40
|
50
|
|
25/09 CuT
|
≈ER2553
|
W 25 9 4 L
|
0.02
|
1.5
|
0.3
|
25.5
|
9.5
|
3.7
|
|
0.8
|
0.2
|
W:0.6
|
AW
|
600
|
750
|
25
|
-40
|
50
|
|
25/14 E-309L
|
ER309L
|
W 23 12 L
|
0.03
|
2.0
|
0.5
|
24.0
|
13.0
|
-
|
|
|
|
|
AW
|
400
|
550
|
30
|
+20
|
55
|
|
25/14 E-309L Si
|
ER309LSi
|
W 23 12 L Si
|
0.03
|
2.0
|
0.9
|
24.0
|
13.0
|
-
|
|
|
|
|
AW
|
400
|
550
|
30
|
+20
|
55
|
|
25/22 H
|
≈ER310
|
W 25 22 2 L N
|
0.025
|
6.0
|
0.2
|
25.0
|
22.5
|
2.2
|
|
|
0.13
|
|
AW
|
400
|
600
|
30
|
+20
|
80
|
|
25/24 R
|
-
|
WZ 25 24 Nb
|
0.32
|
1.4
|
0.6
|
25.0
|
24.0
|
|
1.3
|
|
|
|
AW
|
400
|
600
|
10
|
-
|
-
|
|
25/35 R
|
-
|
WZ 25 35
|
0.42
|
1.8
|
1.2
|
26.0
|
35.0
|
-
|
1.3
|
|
|
|
AW
|
400
|
600
|
8
|
-
|
-
|
|
25/35 Zr
|
-
|
WZ 25 35 Zr
|
0.42
|
1.8
|
1.2
|
26.0
|
35.0
|
|
1.3
|
|
|
Zr<0.15
|
AW
|
400
|
600
|
8
|
-
|
-
|
|
30/10
|
≈ER312
|
W 29 9
|
0.15
|
1.6
|
0.5
|
30.0
|
9.0
|
-
|
|
|
|
|
AW
|
500
|
750
|
20
|
+20
|
27
|
|
35/45 Nb
|
-
|
WZ 35 45 Nb H
|
0.42
|
1.0
|
1.5
|
35.0
|
45.5
|
|
0.8
|
|
|
|
AW
|
245
|
450
|
6
|
-
|
-
|
|
30/40 E
|
≈ER383
|
SG-NiCr 29 Mo*
|
0.02
|
2.6
|
0.2
|
29.0
|
36.0
|
4.3
|
1.8
|
|
|
|
AW
|
350
|
550
|
30
|
+20
|
75
|
|
|
鎳基合金鎢極氬弧焊實心焊絲(GTAW rods
for Ni Base Alloys)
|
產品牌號
Thermanit…
|
分類標準及標號
|
基本化學成份典型值(%)海焊焊材
|
熱處理
|
σ0.2
|
σb
|
δ5
|
AKW
|
|
AWS A5.14/A5.9*
|
DIN1736
|
C
|
Mn
|
Si
|
Cr
|
Ni
|
Mo
|
Nb
|
Fe
|
Co
|
其它
|
MPa
≥
|
MPa
≥
|
%
≥
|
℃
|
J
≥
|
|
30/40E
|
≈ER383*
|
SG-NiCr 29 Mo
|
0.02
|
2.6
|
0.2
|
29.0
|
36.0
|
4.3
|
1.8
|
|
|
|
AW
|
350
|
550
|
30
|
+20
|
75
|
|
617
|
ERNiCRCoMo-1
|
SG-NiCr 22 Co 12 Mo
|
0.05
|
0.2
|
0.2
|
21.0
|
余量
|
9.0
|
|
2.0
|
12.0
|
Al:1.0
Ti:0.5
|
AW
|
400
|
700
|
30
|
+20
|
60
|
|
625
|
ERNiCrMo-3
|
SG-NiCr21Mo9
|
0.02
|
2.8
|
0.2
|
19.5
|
余量
|
-
|
|
|
|
|
AW
|
380
|
620
|
35
|
+20
|
90
|
|