A continuous solid nickel based electrode alloyed with 30 % Cu for welding of base materials of the same type. Can also be used to join these alloys to steel. The weld metal has good resistance to flowing seawater and has high strength and toughness over a rather wide temperature range. Has also good resistance to hydrofluoric acid, sulphuric acid, alkalis etc. Can be used for welding of similar types of base materials which are age-hardenable with small additions of Ti and Al. Usable for cladding on carbon steel with an intermediate layer of OK Autrod 19.92.
Approvals are based on factory location. Please contact ESAB for more information.
瑞典伊薩公司的歷史是從1904年奧斯卡·卡爾伯格（Oscar Kjellbrg）先生發明藥皮焊條開始的時至今日，伊薩的焊材仍然采用OK命名，使我們想起伊薩公司在焊接領域百年的發展壯大歷程。
種類
ESAB
技術標準
熔敷金屬力學性能
熔敷金屬化學成分（％）
SFA/AWS
DIN 1736
屈服值Mpa
抗拉強度Mpa
延伸率％
沖擊值
C
Si
Mn
Cr
Ni
Mo
其它
手工焊條
OK 92.05
A5.11 ENi-1
EL-NiTi3
320
450
25
0.05
1.0
0.7
－
92.0
－
Ti3.0
OK 92.15
A5.11
EL-NiCr15FeNb
420
660
45
+20 ℃ 110
＜ 0.1
0.5
2.0
15.5
70.0
2.0
Nb2.0
OK 92.26
A5.11-90
EL-NiCr15FeMn
410
640
40
+20 ℃ 100
＜ 0.1
0.6
6.0
16.0
70.0
－
Nb2.0
OK 92.45
A5.11
EL-NiCr20Mo9 Nb
480
800
40
+20 ℃ 70
＜ 0.03
0.4
0.4
22.0
64.0
9.5
Nb3.3
OK 92.55
A5.11
460
705
40
+20 ℃ 95
＜ 0.08
0.7
3.0
13.0
70.0
6.5
Nb1.3
OK 92.59
EL-NiCr22Mo16
430
不銹鋼焊條
種類
ESAB牌號
技術標準
熔敷金屬力學性能
熔敷金屬化學成分（％）
SFA/AWS
EN
屈服值Mpa
抗拉強度Mpa
延伸率％
沖擊值J
C
Si
Mn
Cr
Ni
其它
手工焊條
OK 61.25
A5.4-9E308-15
EN 1600E 19 9 H B 22
430
600
45
20℃ 70
0.06
0.5
1.7
18.5
9.5
－
OK 61.30
A5.4 E308L-17
EN 1600 E 19 9 L R 12
430
560
45
20℃ 70
0.03
0.8
0.7
19.5
10.0
－
OK 61.35
A5.4 E308L-15
EN1600E 19 9 L B 2 2
460
580
45
+20℃ 100-120℃ 70-196℃ 45
0.03
0.4
1.7
19.5
10.5
－
OK 61.41
A5.4 E308L-17
EN1600 E 19 9 L R 5 3
420
560
45
20℃ 65
0.03
0.7
0.8
19.5
10.0
－
OK 61.50
A5.4-92 E308H-17
EN1600 E 19 9 H R 12
430
600
45
20℃ 60
0.05
0.8
0.8
20.0
10.
－
OK 61.80
A5.4-92 E347-17
EN 1600E 19 9 Nb R 12
500
630
40
+20℃ 60-80℃ 40
0.03
0.7
0.6
20.0
10.0
Nb 0.3
OK 61.81
A5.4 E347-16
EN1600 E 19 9 Nb R 3 2
560
700
32
+20℃ 60
0.06
0.6
1.6
20.0
10.0
Nb 0.7
OK 61.85
A5.4 E347-15
EN1600 E 19 9 Nb B 2 2
500
620
40
+20℃ 100-60℃ 70
0.05
0.5
1.7
19.5
10.0
Nb 0.5
OK 61.86
A5.4 E347-17
EN1600 E 19 9 Nb R 1 2
520
660
35
+20℃ 55
0.03
0.7
0.8
19.0
10.0
Nb 0.3
OK 63.20
A5.4 E316L-16
EN1600 E 19 12 3 L R 1 1
480
580
35
+20℃ 65-60℃ 45-120℃ 32
0.03
0.7
0.8
18.5
12.0
Mo2.8
OK 63.30
A5.4 E316L-17
EN1600 E 19 12 3 L R 1 2
460
570
40
+20℃ 60-125℃ 32
0.03
0.8
0.6
18.0
12.0
Mo2.8
OK 63.31
A5.4 E316L-17
EN1600 E 19 12 3 L R 3 2
460
570
38
+20℃ 60-125℃ 35
0.03
0.8
0.7
19.0
11.0
Mo2.8
OK 63.34
A5.4 E316L-16
EN1600 E 19 12 3 L R 11
440
600
40
+20℃ 65
0.03
0.8
0.8
18.5
12.0
Mo2.8
OK 63.35
A5.4 E316L-15
EN1600E 19 12 3 L B 2 2
460
600
35
+20℃ 95-120℃ 60-196℃ 35
0.03
0.5
1.7
18.5
12.6
Mo2.8
OK 63.41
A5.4 E316L-17
EN1600 E 19 12 3 L R 5 3
430
570
45
+20℃ 60
0.03
0.8
0.7
18.0
12.0
Mo2.8
OK 63.80
A5.4 E318-17
EN 1600E 19 12 3 Nb R 3 2
500
620
35
+20℃ 55
0.02
0.8
0.6
18.0
12.0
Mo2.8Nb0.3
OK 64.30
A5.4 E317L-17
EN1600 E 19 13 4 LR 3 2
480
600
30
+20℃ 45
0.03
0.7
0.7
19.0
13.0
Mo2.8
OK 67.13
A5.4 E310-16
EN 1600 E 25 20 R 12
560
600
35
+20℃ 60
0.1
0.5
1.9
26.0
21.0
－
OK 67.15
A5.4 E310-15
EN 1600 E 25 20 B 22
410
590
35
+20℃ 100
0.1
0.3
2.0
26.0
20.0
－
OK 67.20
A5.4 E309MoL-16
EN1600 E 23 12 2 LR 1 1
480
640
35
+20℃ 60
0.03
0.8
0.8
23.0
13.0
Mo2.9
OK 67.50
A5.4 E2209-17
EN 1600E 22 9 3 N L R 3 2
660
820
25
+20℃ 70
0.03
0.8
1.0
23.0
9.0
Mo3.0N0.15
OK 67.55
A5.4 E2209-15
EN 1600E 22 9 3 N L B 2 2
650
800
28
+20℃ 100-40℃ 75-60℃ 65
0.03
0.7
1.0
23.0
9.0
Mo3.0N0.15
OK 67.60
A5.4 E309L-17
EN 1600E 23 12 L R 3 2
470
580
32
+20℃ 50-10℃ 40
0.03
0.8
0.9
24.0
12.5
－
OK 67.62
A5.4 E309-26
EN1600 E 23 12 R 7 3
450
570
40
+20℃ 60
0.05
0.8
0.6
24.0
12.5
－
OK 67.66
A5.4 E309L-16
EN1600 E 23 23 L R 3 2
430
580
45
+20℃ 70
0.03
0.4
1.0
23.0
13.0
－
OK 67.70
A5.4 E309MoL-17
EN1600 E 23 12 2 LR 3 2
510
620
33
+20℃ 50
0.03
0.8
0.6
23.0
13.0
Mo2.7
OK 67.75
A5.4 E309L-15
EN1600 E 23 12 L B 4 2
460
570
35
+20℃ 75-80℃ 55
0.03
0.3
0.2
24.0
13.0
Mo0.3
OK 68.15
A5.4 E410-15
EN1600 E 13 B 4 2
390
520
25
+20℃ 55
0.06
0.5
0.5
13.0
－
－
OK 68.17
A5.4 E410NiMo-16
EN 1600E 13 4 R 3 2
650
870
17
+20℃ 45-10℃ 45-40℃ 40
0.03
0.4
0.6
12.0
4.6
Mo0.6
OK 68.25
A5.4E410NiMo-15
EN 1600E 13 4 B 4 2
680
880
17
+20℃ 60-20℃ 53
0.03
0.4
0.6
12.5
4.5
Mo0.6
OK 68.60
EN 1600 E 25 4 R 3 2
660
800
15
+20℃ 30
0.05
1.1
1.2
26
5
Mo1.5N0.18
OK 68.81
A5.4 E312-17
EN1600 E 29 9 R 3 2
580
750
25
+20℃ 30
0.12
0.7
0.8
29.0
10.0
－
OK 69.25
EN 1600E 20 16 3 Mn L B 4 2
450
650
30
+20℃ 90-196℃ 50
0.03
0.5
6.5
19.0
16.0
Mo3.0N0.15
OK 69.33
A5.4E385-16
EN 1600E 20 25 5 Cu N L R 3 2
400
575
35
+20℃ 80-140℃ 45
0.03
0.5
1.0
20.5
25.0
Mo5.0Cu1.5
低合金鋼焊條
種類
ESAB
技術標準
熔敷金屬力學性能
熔敷金屬化學成分（％）
SFA/AWS
EN
屈服值Mpa
抗拉強度Mpa
延伸率％
沖擊值
C
Si
Mn
Ni
Cr
Mo
手工焊條
OK 48.08
A5.5-96 E7018-G
EN 499
540
600
26
-20 ℃ 160
0.06
0.35
1.2
0.9
－
－
OK 73.15
A5.5
EN 499
550
610
28
-50 ℃ 120
0.06
0.4
1.4
0.9
－
－
OK 73.68
A5.5
EN 499
520
610
26
-55 ℃ 110
0.05
0.35
1.0
2.4
－
－
OK 73.79
A5.5
EN 499
520
610
26
-60 ℃ 160
0.06
0.3
0.6
3.3
－
－
OK 74.46
A5.5
EN 1599
460
560
27
+20 ℃ 175
0.06
0.3
0.8
－
－
0.5
OK 74.70
A5.5
EN 499
540
630
26
-20 ℃ 110
0.08
0.4
1.5
－
－
0.4
OK 74.78
A5.5
EN 1599
600
650
24
0 ℃ 100
0.06
0.35
1.5
－
－
0.35
OK 75.75
A5.5 E11018-G
EN 757
755
820
20
-20 ℃ 85
0.05
0.35
1.75
2.25
0.45
0.45
OK 75.78
EN757 E89 6 Mn3NiCrMo B 42 H5
920
965
17
-60 ℃ 60
0.05
0.3
2.1
3.1
0.5
0.6
OK 76.18
A5.5 E8018-B2
EN 1599
530
620
20
+20 ℃ 120
0.06
0.3
0.7
－
1.3
0.5
OK 76.28
A5.5
EN 1599
550
650
18
+20 ℃ 120
0.06
0.3
0.7
－
2.3
1.1
OK76.35
A5.5
EN 1599
/
460
35
+20 ℃ 145
0.05
0.4
0.7
－
5.0
0.55
OK 76.96
A5.5 E8015-B8
EN 1599 E CrMo 9 B
/
＞ 450
＞ 20
+20 ℃＞ 80
0.05
0.5
0.8
－
9.5
1.0
OK 78.16
A5.5 E9018-G
870
900
18
規格
Consumable Characteristics
Alloy Type
Alloyed nickel (Ni + 30 % Cu + 2 % Ti + 2 % Fe)
分類
ERNiCu-7
SFA/AWS A5.14
S Ni 4060 (NiCu30Mn3Ti)
EN ISO 18274
焊縫金屬分析
Analysis Type
3
元素
C
額定百分比
0.03 %
Analysis Type
3
元素
Si
額定百分比
0.3 %
熔敷數據
安培
100-200 A
熔敷率
2,5-5,5 kg/h
電壓 V
21-27 V
直徑
1.0 mm
送絲速度
6-13 m/min
分類:
ERNiCu-7,SFA/AWS A5.14,S Ni 4060 (NiCu30Mn3Ti),EN ISO 18274
認證:
01554 (MV),VdTüV,06276 (FP),VdTüV
Alloy Type:
Alloyed nickel (Ni + 30 % Cu + 2 % Ti + 2 % Fe)
熔敷數據
安培
熔敷率
電壓 V
直徑
送絲速度
As welded
100-200 A
2,5-5,5 kg/h
21-27 V
1.0 mm
6-13 m/min
品牌：瑞典伊薩
伊薩公司悠久的歷史和不斷發展壯大的努力使得伊薩公司成為焊接和切割領域****的公司。
伊薩公司的第一個發明是藥皮焊條。隨之而來的是伊薩在全世界的工程師們為工業界帶來無數發明創造。其中包括一些焊接領域重要的突破，如擠壓藥皮焊條、埋弧焊（Unionmelt）、鐵粉低氫焊條，MIG焊、TIG焊（Heliarc）、第一個使用氣體保護藥芯焊絲（Dualshield）第一個使用全位置藥芯焊絲、等離子切割和焊接以及其他一些對焊接質量和提高生產率有重大影響的方法。時至今日，伊薩公司仍然是焊接新產品、新工藝的倡導者，如摩擦攪拌焊，獨特的藥芯焊絲焊接鑄鐵，高強焊絲焊接特殊的高強鋼。伊薩這種保持領先的傳統使其成為您在焊接和切割方面的最佳伙伴。
鎳基合金焊條
牌號
J
Fe0.7
EniCrFe-2
-196 ℃ 90
Fe8.0
EniCrFe-3
-196 ℃ 80
Fe6.0
EniCrMo-3
-196 ℃ 50
Fe3.0
ENiCrMo-6
-60 ℃ 90
-196 ℃ 80
Fe4.0
W1.5
牌號
J
E 46 5 1 Ni B 32 H5
-40 ℃ 130
-50 ℃ 100
-60 ℃ 60
E7018-G
E 46 5 Mn 1Ni B 42 H5
E8018-C1
E 46 6 2Ni B 32 H5
-60 ℃ 105
E8016-C2
E 46 6 3Ni B 12
-73 ℃ 90
-95 ℃ 40
-101 ℃ 35
E7018-A1
E Mo B 42
-20 ℃ 100
E8018-G
E 46 MnMo B 32
-40 ℃ 80
-60 ℃ 50
E9018-D1
E Mo B42
-20 ℃ 90
-30 ℃ 75
-40 ℃ 60
E 69 5 Mn2 NiCrMoB 42 H5
-40 ℃ 70
-51 ℃ 55
-60 ℃ 45
E CrMo 1 B 42 H5
E9018-B3
E CrMo 2 B 42 H5
E8015-B6
E CrMo 5 B 32 H5
-20 ℃ 75